ASTM E3100-22 PDF

SIGNIFICANCE AND USE 5.1 Real-time detection and assessment of cracks and other flaws in concrete structures is of great importance. A number of methods have been developed and standardized in recent decades for non-destructive evaluation of concrete structures as well as methods for in-place evaluation of concrete properties. Review of some of these methods can be found in ACI 228.2R-13, ACI 228.1R-03, and ACI 437R-03. They include visual inspection, stress-wave methods such as impact echo, pulse velocity, impulse response, nuclear methods, active and passive infrared thermography, ground-penetrating radar and others. These methods in most of the cases are not used for overall inspection of the concrete structure due to limited accessibility, significant thickness of concrete components, or other reasons and are not applied for continuous long-term monitoring. Further, these methods cannot be utilized for estimation of flaw propagation rate or evaluation of flaw sensitivity to operational level loads or environmental changes, or both. 5.2 In addition to the previously mentioned non-destructive tests methods, vibration, displacement, tilt, shock, strain monitoring, and other methods have been applied to monitor, periodically or continuously, various factors that can affect the integrity of concrete structures during operation. However, these methods monitor risk factors that are not necessarily associated with actual damage accumulation in the monitored structures. 5.3 Monitoring the opening or elongation of existing cracks can be performed as well using different technologies. These may include moving scales (Fig. 1), vibrating wire, draw wire, or other crack opening displacement meters, optical and digital microscopes, strain gages, or visual assessment. However, this type of monitoring is only applicable to surface cracks and requires long monitoring periods. FIG. 1 Moving Scale Crack Opening Monitor 5.4 This guide is meant to be used for development of acoustic emission a... SCOPE 1.1 This guide describes the application of acoustic emission (AE) technology for examination of concrete and reinforced concrete structures during or after construction, or in service. 1.2 Structures under consideration include but are not limited to buildings, bridges, hydraulic structures, tunnels, decks, pre/post-tensioned (PT) structures, piers, nuclear containment units, storage tanks, and associated structural elements. 1.3 AE examinations may be conducted periodically (short-term) or monitored continuously (long-term), under normal service conditions or under specially designed loading procedures. Examples of typical examinations are the detection of growing cracks in structures or their elements under normal service conditions or during controlled load testing, long term monitoring of pre-stressed cables, and establishing safe operational loads. 1.4 AE examination results are achieved through detection, location, and characterization of active AE sources within concrete and reinforced concrete. Such sources include micro- and macro-crack development in concrete due to loading scenarios such as fatigue, overload, settlement, impact, seismicity, fire and explosion, and also environmental effects such as temperature gradients and internal or external chemical attack (such as sulfate attack and alkali-silica reaction) or radiation. Other AE source mechanisms include corrosion of rebar or other metal parts, corrosion and rupture of cables in pre-stressed concrete, as well as friction due to structural movement or instability, or both. 1.5 This guide discusses selection of the AE apparatus, setup, system performance verification, detection and processing of concrete damage related AE activity. The guide also provides approaches that may be used in analysis and interpretation of acoustic emission data, assessment of examination results and establishing accept/reject criteria. 1.6 Units—The values stated ...