ASTM F2952-22 PDF

SIGNIFICANCE AND USE 4.1 This document describes the basic principles that need to be followed to obtain a mean value of the Darcy permeability coefficient for structures that consist of a series of interconnected voids or pores. The coefficient is a measure of the permeability of the structure to fluid flowing through it that is driven by a pressure gradient created across it. 4.2 The technique is not sensitive to the presence of closed or blind-end pores (Fig. 1). FIG. 1 Schematic of the Different Pores Types Found in Tissue Scaffolds. Fluid Flow Through the Structure is via the Open Pores 4.3 Values of the permeability coefficient can be used to compare the consistency of manufactured samples or to determine what the effect of changing one or more manufacturing settings has on permeability. They can also be used to assess the homogeneity and anisotropy of tissue scaffolds. Variability in the permeability coefficient can be also be indicative of: 4.3.1 Internal damage within the sample, for example, cracking or permanent deformation. 4.3.2 The presence of large voids, including trapped air bubbles, within the structure. 4.3.3 Surface effects such as a skin formed during manufacture. 4.3.4 Variable sample geometry. 4.4 This test method is based on the assumption that the flow rate through a given sample subjected to an applied pressure gradient is constant with time. Note 1: If a steady-state flow condition isn’t reached, then this could be due to structural damage (that is, crack formation or the porous structure deformed as a result of the force being placed upon it by the fluid flowing through it). Sample deformation in the form of stretching (bowing) can also occur for less resilient structures as a result of high fluid flow rates. This topic is discussed in more detail in Section 7. 4.5 Care should be taken to ensure that hydrophobic materials are fully wetted out when using water or other aqueous-based liquids as permeants. 4.6 Conventionally, the p... SCOPE 1.1 This guide describes test methods suitable for determining the mean Darcy permeability coefficient for a porous tissue scaffold, which is a measure of the rate at which a fluid, typically air or water, flows through it in response to an applied pressure gradient. This information can be used to optimize the structure of tissue scaffolds, to develop a consistent manufacturing process, and for quality assurance purposes. 1.2 The method is generally nondestructive and non-contaminating. 1.3 The method is not suitable for structures that are easily deformed or damaged. Some experimentation is usually required to assess the suitability of permeability testing for a particular material/structure and to optimize the experimental conditions. 1.4 Measures of permeability should not be considered as definitive metrics of the structure of porous tissue scaffolds and should complement measures obtained by other investigative techniques, for example, scanning electron microscopy, gas flow porometry, and micro-computer X-ray tomography (Guides F2450, F2603, and F3259). 1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.