ISO 14627:2012

Name: ISO 14627:2012 — Fine ceramics (advanced ceramics, advanced technical ceramics) — Test method for fracture resistance of silicon nitride materials for rolling bearing balls at room temperature by indentation fracture (IF) method
SKU: ISO 14627:2012
Price: 25 EUR
Availability: InStock

Fine ceramics (advanced ceramics, advanced technical ceramics) — Test method for fracture resistance of silicon nitride materials for rolling bearing balls at room temperature by indentation fracture (IF) method

Название (английский):

ISO 14627:2012

Статус документа:: Действующий
Формат:: Электронный (PDF)
Количество страниц:: 8
Дата публикации:: 6 июля 2012 г.
Издание:: ISO IS 14627 edition 1 version 1
ICS:: 81.060.30

Тип поставки:

Full version25 €Ask AI2 €Read online 24h10 €Read online 72h15 €

Язык документа:

ruen

Срок поставки:1 рабочий день

Цена:25 €

Описание (английский):

ISO 14627:2012 describes a test method that covers the determination of fracture resistance of silicon nitride bearing balls at room temperature by the indentation fracture (IF) method, as specified in ISO 26602. ISO 14627:2012 is intended for use with monolithic silicon nitride ceramics for bearing balls. It does not include other ceramic materials. ISO 14627:2012 is for material comparison and quality assurance.

Abstract

Похожие стандарты

Стандарты, упомянутые в описании

Overview - ISO 14627:2012 (silicon nitride fracture resistance by IF)

ISO 14627:2012 specifies an indentation fracture (IF) test method for determining the fracture resistance of monolithic silicon nitride materials used for rolling bearing balls at room temperature. Intended for material comparison and quality assurance, the standard defines the Vickers indentation procedure (per ISO 26602) to produce and measure indentation cracks and calculate an IF-based fracture resistance value (KI,IFR). It is not a substitute for conventional fracture toughness (KIc) tests - KI,IFR estimates resistance to crack initiation/extension from localized damage.

Key topics and technical requirements

Scope: Applies only to monolithic silicon nitride bearing balls; excludes other ceramics. Used for QA and material comparison.

Test principle: Force a Vickers (diamond pyramid) indenter into a polished specimen, measure indent diagonals (2a) and crack lengths (2c), and compute KI,IFR using Niihara’s equation.

Loading and timing:

Typical load: 196.1 N with 15 s dwell time; if unacceptable indentations appear, 98.07 N may be used (report the load used).

Specimen requirements:

Use ground and polished surfaces; remove grinding-induced residual stress.
Thickness: generally > 3 mm and at least 5× the crack length (2c) to avoid edge effects.
Surface roughness Ra ≤ 0.1 µm (ISO 4287).

Indentation acceptability and sampling:

At least 5 valid indentations per test; spacing ≥ 5× diagonal crack length and ≥ 3× from specimen edge.
Reject asymmetric, forked, or chipped indentations; horizontal/vertical crack lengths must agree within 10%.

Measurements & precision:

Measure 2a to within 2 µm and 2c to within 10 µm, preferably using ≥100× (ideally ≥200×) magnification; measurements within 10 minutes after unloading.
Elastic modulus E obtained by sonic resonance (ISO 17561) or literature if same-lot specimen unavailable.

Calculations & reporting:

HV and KI,IFR formulae given (Niihara method); test report aligned to ISO/IEC 17025 requirements and must document specimen, E, loads, magnification, batch data and results.

Practical applications and users

Bearing manufacturers and component suppliers for incoming material inspection and lot-to-lot comparison.

Ceramic material producers for process control and verification of silicon nitride grades.

Independent testing/QA laboratories applying ISO/IEC 17025 accreditation.

R&D and tribology teams correlating indentation fracture resistance with wear resistance and rolling contact fatigue performance.

Use cases: production quality control, supplier qualification, comparative evaluation of silicon nitride lots, and process improvement (machining, finishing).

Related standards

ISO 26602 - Silicon nitride materials for rolling bearing balls (method context)

ISO 6507-2 / ISO 6507-3 - Vickers hardness testing and reference blocks

ISO 17561 - Elastic moduli by sonic resonance

ISO 4287 - Surface texture (Ra definition)

ISO/IEC 17025 - Testing laboratory competence

Keywords: ISO 14627, silicon nitride, indentation fracture (IF) method, Vickers indenter, bearing balls, fracture resistance, material comparison, quality assurance.

ISO 14627:2012

Abstract

Похожие стандарты

Overview - ISO 14627:2012 (silicon nitride fracture resistance by IF)

Key topics and technical requirements

Practical applications and users

Related standards

Технические детали

BS ISO 26602:2017

Fine ceramics (advanced ceramics, advanced technical ceramics). Silicon nitride materials for rolling bearing…

ISO 4287:1997

Geometrical Product Specifications (GPS) — Surface texture: Profile method — Terms, definitions and surface t…

BS ISO 17561:2016

Fine ceramics (advanced ceramics, advanced technical ceramics). Test method for elastic moduli of monolithic…

BS EN ISO/IEC 17025:2017

General requirements for the competence of testing and calibration laboratories.

ISO 6507-2:2018

Metallic materials — Vickers hardness test — Part 2: Verification and calibration of testing machines

ISO 6507-3:2018

Metallic materials — Vickers hardness test — Part 3: Calibration of reference blocks