ISO 7905-3:2019 PDF

Name: ISO 7905-3:2019 — Plain bearings — Bearing fatigue — Part 3: Test on plain strips of a metallic multilayer bearing material
SKU: ISO 7905-3:2019
Price: 25 EUR
Availability: InStock

Plain bearings — Bearing fatigue — Part 3: Test on plain strips of a metallic multilayer bearing material

Название (английский):

ISO 7905-3:2019

Plain bearings — Bearing fatigue — Part 3: Test on plain strips of a metallic multilayer bearing material

Статус документа:: Действующий
Формат:: Электронный (PDF)
Количество страниц:: 9
Дата публикации:: 9 апреля 2019 г.
Издание:: ISO IS 7905 edition 2 version 1
ICS:: 21.100.10

Тип поставки:

Full version135 €Read online 24h10 €Read online 72h15 €

Язык документа:

ruen

Срок поставки:2 раб. дн. (перевод)

Цена:135 €

Описание (английский):

This document specifies a method for the determination of the endurance limit in fatigue of plain strips of multilayer bearing materials. Additionally, it provides the opportunity of studying the influence on the strips of hydraulic pressure and variable temperature.

Abstract

Похожие стандарты

Стандарты, упомянутые в описании

Overview

ISO 7905-3:2019 specifies a laboratory method to determine the endurance limit in fatigue of plain strips made from metallic multilayer bearing materials. The standard covers specimen preparation, a cyclic bending test procedure that reproduces tension–compression loading over the running surface, and evaluation and presentation of fatigue results. The method also allows assessment of the influence of hydraulic pressure and variable temperature on fatigue performance.

Key topics and technical requirements

Test specimens: flat thin rectangular strips with chamfered edges and a contoured test section; layer thickness and surface texture must be representative of the actual manufacturing sequence and finishing.

Test principle: cantilever-style clamping at one end with cyclic loading at the free end producing bending from tension to compression; optional tensile or compressive prestress to study mean-stress effects.

Environment: tests performed in lubricant-filled chambers or in air at controlled temperatures (±2 °C).

Instrumentation and control:

Bending stress measured by a strain gauge near the clamp on the specimen back.
Load amplitude controlled by force or displacement; test frequency range 50–80 Hz.
Crack detection by dye penetrant or microscope.

Result presentation and evaluation:

Endurance limits presented as σ–N (stress vs. cycles) curves and optionally as Haigh diagrams (stress amplitude vs mean stress).
Typical termination and endurance points may be quoted at specified cycle counts (e.g., 3×10^6, 10×10^6, 25×10^6, 50×10^6 cycles); statistical methods recommended to address scatter.
Metallographic examination to identify damage mechanisms, corrosion, and thermal diffusion effects.

Limitations: the method does not capture residual stresses introduced by some bearing manufacturing processes.

Applications and practical value

Assess fatigue performance and endurance limits of multilayer plain bearing linings.

Compare bearing material formulations, layer sequences and surface finishes under controlled cyclic loading.

Investigate effects of temperature, hydraulic pressure, and mean stress on bearing fatigue life.

Support material selection, quality control, failure analysis, and R&D for plain bearing systems.

Keywords: ISO 7905-3, plain bearings, bearing fatigue, multilayer bearing material, endurance limit, fatigue testing, strain gauge, σ–N curve, Haigh diagram.

ISO 7905-3:2019 PDF

Abstract

Похожие стандарты

Overview

Key topics and technical requirements

Applications and practical value

Who should use this standard

Related standards

Технические детали

SIST ISO 7905-3:2020

Plain bearings - Bearing fatigue - Part 3: Test on plain strips of a metallic multilayer bearing material

ISO 3548-1:2022/Amd 1:2024

Plain bearings — Thin-walled half bearings with or without flange — Part 1: Tolerances, design features and m…

SIST ISO 4378-1:2020

Plain bearings - Terms, definitions, classification and symbols - Part 1: Design, bearing materials and their…