Role of Dislocations, Dislocation Walls, and Grain Boundaries in Void Formation During Early Stages of Fast Neutron Irradiation
Название (английский):
ASTM STP37366S
Role of Dislocations, Dislocation Walls, and Grain Boundaries in Void Formation During Early Stages of Fast Neutron Irradiation
- Статус документа:
- D
- Формат:
- Электронный (PDF)
- SKU:
- ASTM STP37366S
Цена по запросу
Свяжитесь с нами для уточнения стоимости.
Abstract
High purity aluminium was used to study the details of microstructural evolution during early stages of neutron irradiation. Aluminium specimens were irradiated at 120°C to fluences between 2.1021 and 1.1024 n/m2 (E > 0.1 MeV). Transmissio...